Promotional effect of silica on the combustion of nano-sized aluminum powder in carbon dioxide

This paper presents how the combustion performance of nano-sized aluminum(nAl)powder in carbon dioxide are affected by silica. The ignition and combustion performance of nAl powder with silica addition were studied by a high-temperature tube furnace. An s-type thermocouple and a high-speed motion acquisition instrument were performed to evaluate the ignition temperature, maximum combustion temperature, maximum change of rate of temperature, and combustion propagation speed. The combustion effici...     

2219铝合金厚板TIG焊接头组织与力学性能研究

采用氦弧打底+氩弧填充、盖面的焊接工艺对2219-T87铝合金15 mm厚板进行TIG焊接试验，研究其焊缝成形和组织力学性能。结果表明，此工艺焊缝成形美观，无可见焊接缺陷，气孔抑制效果好，接头平均抗拉强度为278.22 MPa，平均断后延伸率为3.89%，接头平均强度系数达到58.94%。接头硬度整体表现为焊缝中心最低，从焊缝中心到母材呈现先增大后局部降低再增大的趋势；且焊缝中心填充层硬度高于打底层和盖面层。熔合区的微观组织为柱状树枝晶和胞状树枝晶，且垂直于熔合线生长，在靠近熔合区两侧出现了等轴细晶带。焊接接头断面有较多撕裂棱和韧窝，局部发现第二相粒子和微孔，其断裂机制为典型的韧性断裂。     

国产5056铝蜂窝芯的制备与性能评价

针对太阳翼基板用高性能低密度5056铝蜂窝芯的需求，开展了国产5056超薄铝箔制备及配套阳极氧化表面处理、国产5056铝蜂窝的制备和性能评价。研制的国产5056铝蜂窝芯公称密度17.28 kg/m³，节点强度为1.87 kN/m，蜂窝芯裸压缩、平面压缩、L向剪切、W向剪切强度分别达到了0.29、0.31、0.38、0.27 MPa，力学性能均达到了进口蜂窝芯的水平。蜂窝芯胶膜热破工艺性能较好，网格夹层结构节点无脱开，弯曲刚度和强度测试值均达到了进口蜂窝测试值的水平，可以满足使用需求。试验结果可为后续高性能低密度铝蜂窝芯的型号应用及原材料国内自主保障提供数据基础及技术基础。     

TiB2/7050颗粒增强铝基复合材料热变形行为与热压工艺优化

分析TiB₂/7050颗粒增强铝基复合材料的热变形行为及工艺参数的影响规律，对其热变形后的组织设计和获得理想性能参数至关重要。基于此，针对TiB₂/7050颗粒增强铝基复合材料开展了相关研究。用Gleeble-3500热模拟机进行热压缩试验，研究了TiB₂/7050颗粒增强铝基复合材料在变形温度300~450 ℃、应变速率0.001~1 s-1时的热变形行为，建立了材料的双曲正弦本构方程；根据动态材料模型计算得出热加工图，优选了材料的热加工工艺窗口；对原始挤压成型坯料和优化工艺的热压成型坯料进行了力学性能测试和微观组织形貌分析。结果表明:两种成型工艺相比，热压件强度指标略有提高，但塑性大幅提高，其长横向断后延伸率提高400%；热压工艺件晶粒更加细小、且无明显择优取向；拉伸断裂机制均为准解理断裂，热压件断口韧窝更深、撕裂棱更粗大，表明塑性撕裂持续时间更长。      

2219 铝合金单、双道焊接头性能分析

通过对比2219 铝合金单道氩弧焊和氦弧打底+氩弧盖面双道焊接头的常温及液氮温度拉伸性
能、显微硬度分布、单向拉伸过程的数字散斑测量(DIC)结果,发现在常、低温条件下双道焊接头的拉伸强度和
延伸率均比单道焊接头高10% ~20%,单道焊接头焊缝及热影响区内材料的显微硬度值相比母材的降低程度
比双道焊接头更为显著,其主要原因是单道焊接头的一次性热输入大于双道焊,材料受热影响更严重,焊漏高
度及形状的可控性更差。     

Through-thickness heterogeneity in creep properties of friction stir welding 7B50-T7451 aluminum alloy thick plate joint: Experiments and modeling

Through-thickness heterogeneity in creep properties of 7B50-T7451 aluminum alloy Friction Stir Welding(FSW) joints was investigated. Creep tests for three slices of the FSW joint were conducted at the temperature of 150–200 °C and applied stress of 60–225 MPa. The theta projection method was used to predict creep curves and minimum creep rate. The results show that the minimum creep rate increases and creep rupture life decreases with the increase of creep temperature and applied stress. Creep p...     

干式铣削Al-50wt%Si高硅铝合金刀具磨损与表面粗糙度评价

本文以Al-50wt%Si高硅铝合金为研究对象，采用单因素试验方法进行无涂层硬质合金刀具干式铣削试验，分析切削参数对刀具磨损和表面粗糙度的影响。结果表明：表面粗糙度受每齿进给量的影响最显著，随每齿进给量的增加而增加，当每齿进给量从0.07 mm/z增加到0.16 mm/z时，表面粗糙度增加2倍；刀具磨损受切削速度的影响最显著，随切削速度的增加而增加，当切削速度从140 m/min增加到260 m/min时，切削总长度降低3倍，而刀具后刀面磨损量仅是260 m/min速度下的0.8倍；表面粗糙度随刀具磨损的增加呈现先增加后降低的变化趋势，切削长度从350 mm增加到1 750 mm，刀具磨损量平均增加4.5倍，而表面粗糙度却下降2倍；硬质合金刀具主要的磨损形式为磨粒磨损、崩刃。